From: Plastic and elastic biomechanical properties of anterior cruciate ligament autografts
Mechanical property | QT vs PT | QT vs HT | PT vs HT |
---|---|---|---|
Cross Sectional Area (mm2) | 0.002 | 0.418 | 0.001 |
Failure Force (N) | 0.986 | 0.032 | 0.110 |
Stiffness (N/mm) | 0.0002 | 0.079 | 0.332 |
Youngs Modulus (MPa) | 0 001 | 0.064 | 0.041 |
Yield Force (N) | > 0.999 | 0.6025 | > 0.999 |
Yield Stress (MPa) | 0.036 | 0.018 | 0.494 |
Yield Strain (mm/mm) | 0.113 | 0.706 | 0.365 |
Failure Stress (MPa) | 0.064 | 0.015 | 0.984 |
Failure Strain (mm/mm) | 0.431 | 0.145 | 0.998 |
Plastic Strain (mm/mm) | 0.852 | 0.150 | 0.056 |
Elongation After Yield (mm) | 0.282 | 0.635 | 0.002 |
Elastic Energy Density (J/m3) | 0.637 | 0.012 | 0.625 |
Toughness (J/m3) | 0.986 | 0.032 | 0.101 |
Plastic Energy Density (J/m3) | 0.494 | 0.043 | 0.362 |