Highly-uniform Group | Elastic Modulus [GPa] | Maximum Force [N] | Bending Strength/Maximum Stress [MPa] | Strain at Maximum Force [%] |
---|---|---|---|---|
Mean ± Standard Deviation | ||||
Femora | ||||
UC-PA (n = 4) | 1.85 ± 0.56 | 178.25 ± 11.87 | 82.80 ± 12.04 | 11.27 ± 1.42 |
UC-PR (n = 3) | 1.98 ± 0.45 | 210.69 ± 5.98 | 100.33 ± 11.58 | 12.69 ± 4.48 |
WB-PA (n = 3) | 2.06 ± 0.32 | 185.35 ± 34.44 | 89.85 ± 14.88 | 10.55 ± 1.17 |
WB-PR (n = 3) | 2.77 ± 0.43 | 202.02 ± 3.00 | 114.86 ± 7.98 | 9.86 ± 1.18 |
SB-PA (n = 4) | 2.18 ± 0.61 | 204.21 ± 17.97 | 105.03 ± 20.43 | 11.27 ± 2.61 |
SB-PR (n = 3) | 1.97 ± 0.23 | 200.55 ± 19.3 | 99.36 ± 3.86 | 10.98 ± 1.69 |
Humeri | ||||
UC-PA (n = 3) | 4.93 ± 1.11 | 111.22 ± 16.77 | 156.19 ± 19.39 | 5.02 ± 0.75 |
UC-PR (n = 3) | 5.64 ± 1.44 | 124.12 ± 2.21 | 162.76 ± 14.61 | 5.43 ± 1.00 |
WB-PA (n = 3) | 4.25 ± 0.43 | 114.15 ± 10.17 | 155.95 ± 10.60 | 5.88 ± 0.61 |
WB-PR (n = 3) | 4.67 ± 0.73 | 105.70 ± 15.37 | 168.31 ± 25.07 | 5.01 ± 0.65 |
SB-PA (n = 3) | 5.17 ± 2.81 | 108.61 ± 15.78 | 164.81 ± 39.55 | 6.07 ± 1.96 |
SB-PR (n = 3) | 4.05 ± 0.11 | 110.70 ± 25.31 | 162.45 ± 43.98 | 4.87 ± 1.21 |